Term: magnetic field strength anisotropy factor
Synonym1:
Synonym2:
Synonym3:
Symbol: TH
Definition: of electrical steel, the ratio of the difference between the peak value of the magnetic field strength H ^ α MathType@MTEF@5@5@+=feaagCart1ev2aqatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbbjxAHXgaruavP1wzZbItLDhis9wBH5garmWu51MyVXgarqqtubsr4rNCHbGeaGqipG0dh9qqWrVepG0dbbL8F4rqqrVepeea0xe9LqFf0xc9q8qqaqFn0lXdHiVcFbIOFHK8Feea0dXdar=Jb9hs0dXdHuk9fr=xfr=xfrpeWZqaaeaaciWacmGadaGadeaabaGaaqaaaOqaaiqadIeagaqcamaaBaaaleaacqaHXoqyaeqaaaaa@37F6@ measured at an angle α to the direction of rolling, and the peak value of the magnetic field strength H ^ 0 MathType@MTEF@5@5@+=feaagCart1ev2aqatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbbjxAHXgaruavP1wzZbItLDhis9wBH5garmWu51MyVXgarqqtubsr4rNCHbGeaGqipG0dh9qqWrVepG0dbbL8F4rqqrVepeea0xe9LqFf0xc9q8qqaqFn0lXdHiVcFbIOFHK8Feea0dXdar=Jb9hs0dXdHuk9fr=xfr=xfrpeWZqaaeaaciWacmGadaGadeaabaGaaqaaaOqaaiqadIeagaqcamaaBaaajeaqbaGaaGimaaqcbawabaaaaa@37BA@ measured along the direction of rolling, to H ^ 0 MathType@MTEF@5@5@+=feaagCart1ev2aqatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbbjxAHXgaruavP1wzZbItLDhis9wBH5garmWu51MyVXgarqqtubsr4rNCHbGeaGqipG0dh9qqWrVepG0dbbL8F4rqqrVepeea0xe9LqFf0xc9q8qqaqFn0lXdHiVcFbIOFHK8Feea0dXdar=Jb9hs0dXdHuk9fr=xfr=xfrpeWZqaaeaaciWacmGadaGadeaabaGaaqaaaOqaaiqadIeagaqcamaaBaaajeaqbaGaaGimaaqcbawabaaaaa@37BA@ , at a stated peak value of the magnetic flux density, the ratio being expressed as a percentage:

T H = H ^ α H ^ 0 H ^ 0 ×100% MathType@MTEF@5@5@+=feaagCart1ev2aqatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbbjxAHXgaruavP1wzZbItLDhis9wBH5garmWu51MyVXgarqqtubsr4rNCHbGeaGqipG0dh9qqWrVepG0dbbL8F4rqqrVepeea0xe9LqFf0xc9q8qqaqFn0lXdHiVcFbIOFHK8Feea0dXdar=Jb9hs0dXdHuk9fr=xfr=xfrpeWZqaaeaaciWacmGadaGadeaabaGaaqaaaOqaaiaadsfadaWgaaqcbawaaiaadIeaaSqabaGccqGH9aqpdaWcaaqaaiqadIeagaqcamaaBaaaleaacqaHXoqyaeqaaOGaeyOeI0IabmisayaajaWaaSbaaKqaGfaacaaIWaaaleqaaaGcbaGabmisayaajaWaaSbaaKqaGfaacaaIWaaaleqaaaaakiabgEna0kaaigdacaaIWaGaaGimaiaaykW7caaMc8Uaciyjaaaa@48BE@

NOTE – The measurements of H ^ α MathType@MTEF@5@5@+=feaagCart1ev2aqatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbbjxAHXgaruavP1wzZbItLDhis9wBH5garmWu51MyVXgarqqtubsr4rNCHbGeaGqipG0dh9qqWrVepG0dbbL8F4rqqrVepeea0xe9LqFf0xc9q8qqaqFn0lXdHiVcFbIOFHK8Feea0dXdar=Jb9hs0dXdHuk9fr=xfr=xfrpeWZqaaeaaciWacmGadaGadeaabaGaaqaaaOqaaiqadIeagaqcamaaBaaaleaacqaHXoqyaeqaaaaa@37F6@ and H ^ 0 MathType@MTEF@5@5@+=feaagCart1ev2aqatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbbjxAHXgaruavP1wzZbItLDhis9wBH5garmWu51MyVXgarqqtubsr4rNCHbGeaGqipG0dh9qqWrVepG0dbbL8F4rqqrVepeea0xe9LqFf0xc9q8qqaqFn0lXdHiVcFbIOFHK8Feea0dXdar=Jb9hs0dXdHuk9fr=xfr=xfrpeWZqaaeaaciWacmGadaGadeaabaGaaqaaaOqaaiqadIeagaqcamaaBaaajeaqbaGaaGimaaqcbawabaaaaa@37BA@ are to be made under the same conditions.


Publication date:1990-10
Source
Replaces:
Internal notes:2017-02-27: "field strength" corrected to "magnetic field strength". See mail exchange with RS and JS 2016-01. JGO

2017-06-02: Cleanup - Remove Attached Image 221-03-401.gif

2017-06-02: Cleanup - Remove Attached Image 221-03-402.gif

2017-06-02: Cleanup - Remove Attached Image 221-03-403.gif
CO remarks:
TC/SC remarks:
VT remarks:
Domain1:
Domain2:
Domain3:
Domain4:
Domain5: