Note 1 to entry: Superconducting films are classified into “thin” and “thick”, although the exact boundary between the two is subject to changes in the fabrication technology. The current definitions are by convention as follows.

- superconducting thin film: superconductor film of average thickness less than a given typical value, assumed conventionally to be 1 µm, that is typically obtained by PVD (physical vapour deposition), CVD (chemical vapour deposition) or other techniques;

- superconducting thick film: superconductor film of average thickness of more than some typical value, assumed conventionally to be between 1 µm to 10 µm, that is typically obtained by screen printing, by doctor blading or by dip-coating methods.

Note 2 to entry: This entry was numbered 815-13-27 in IEC 60050-815:2015.

Note 1 à l’article: Les films supraconduceurs sont classés en “minces” et “épais”, bien que la limite exacte entre les deux dépende des changements dans les techniques de fabrication. Les définitions habituelles sont les suivantes par convention:

- film fin supraconducteur: film supraconducteur d'une épaisseur moyenne inférieure à une valeur type, prise conventionnellement égale à 1 µm, généralement obtenu par dépôt physique en phase vapeur (PVD - Physical Vapour Deposition), dépôt chimique en phase vapeur (CVD - Chemical Vapour Deposition) ou toute autre technique.

- film supraconducteur épais: film supraconducteur d'une épaisseur moyenne supérieure à une valeur type, prise conventionnellement entre 1 µm et 10 µm, généralement obtenu par sérigraphie, par la méthode par raclage ou par immersion.

Note 2 à l’article: Cet article était numéroté 815-13-27 dans l’IEC 60050-815:2015.