Note 1 to entry: Cu/Nb or Cu/V mixtures in which Nb or V dendritically form from the melt are processed into wire or tape to give fine internal filamentary forms of Nb or V in a copper matrix, and Nb₃Sn or V₃Ga are formed by the diffusion process.

Note 2 to entry: The in-situ process also includes a production process of a superconducting thin film grown in a single step process.

Note 3 to entry: The in-situ process also includes a production process of MgB₂ wires in which a mixture of magnesium and boron powders or their powdered compounds are filled in a metal tube with heat treatment for reaction after the drawing.

Note 4 to entry: This entry was numbered 815-14-14 in IEC 60050-815:2015.

Note 1 à l’article: Les mélanges Cu/Nb ou Cu/V dans lesquels les dendrites de Nb ou de V se forment à partir de la fusion sont conditionnés en fils ou en bandes pour donner des filaments fins de Nb ou de V dans une une matrice de cuivre, et les composés de type Nb₃Sn ou V₃Ga sont formés par le procédé de diffusion.

Note 2 à l’article: Le procédé in situ comprend aussi un processus de fabrication d’une couche mince supraconductrice formée en une seule étape.

Note 3 à l’article: Le procédé in situ comprend aussi un processus de fabrication de fils MgB₂ au cours duquel un tube de métal est rempli d’un mélange de poudres de magnésium et de bore ou leurs composés en poudre, avec traitement thermique de réaction après l’étirage.

Note 4 à l’article: Cet article était numéroté 815-14-14 dans l’IEC 60050-815:2015.